Laboratory Performance Characteristics of Cold-Mixed Reclaimed Asphalt Pavement(RAP)

Kim, Nak-Seok; Jo, Myoung-Hwan; Im, Jung-Soon

Journal of the Korean Society of Hazard Mitigation 2003;3(1):133-140.
Published online March 31, 2003.

상온재생공법활용 회수아스팔트 혼합물의 실험적 공용특성

김낙석, 조명환, 임정순

Laboratory Performance Characteristics of Cold-Mixed Reclaimed Asphalt Pavement(RAP)

Nak-Seok Kim, Myoung-Hwan Jo, Jung-Soon Im

Abstract

The research was performed to evaluate the cracking resistance characteristics of cold-mixed reclaimed asphalt pavement (RAP) using indirect tensile strength test and fatigue tests. Indirect tensile tests were conducted to estimate the indirect tensile strength at variable temperatures($10^{circ}C;and;20^{circ}C$). Fatigue tests were also carried out using 500kgf, 400kgf, and 300kgf of dynamic loads, and the fatigue life (Nf) for each mixture was measured. Indirect tensile strength of cold-mixed reclaimed asphalt pavement was about 90% of conventional 13mm dense-graded asphalt mixture. Fatigue life of cold-mixed reclaimed asphalt mixture was 70%, 55%, 30% (for 500kgf, 400kgf, 300kgf of load level, respectively) of the conventional one.

Key Words: Reclaimed asphalt pavement(RAP); Cracking resistance; Fatigue life; Cold-Mixed; Indirect tensile strength

요지

본 연구에서는 회수아스팔트 혼합물의 재활용을 위해서 상온재생 아스팔트 혼합물과 재래식 밀입도 13mm 아스팔트 혼합물을 사용하여 아스팔트 혼합물의 실험적 공용특성을 파악하기 위하여 간접인장강도 시험과 피로파괴 시험을 수행하였다. 간접인장강도 시험은 $10^{circ}C,;20^{circ}C$에서 수행되었으며, 피로파괴시험은 500kgf, 400kgf 그리고 300kgf의 반복하중 아래에서 수행되었다. 간접인장강도 시험결과 재생 아스팔트 혼합물은 재래식 아스팔트 혼합물에 대해서 각 온도대별 약 90%의 성능을 보였으며, 피로파괴 시험의 결과에 의하면 재생 밀입도 아스팔트 혼합물은 반복하중 500kgf, 400kgf, 및 300kgf에 대해서 각각 재래식 아스팔트 혼합물의 70%, 55%, 30%의 성능을 보여주었다.

핵심용어: 회수아스팔트 포장; 균열저항; 피로수명; 상온혼합; 간접인장강도