Experimental Performance Characteristics of Crumb Rubber-Modified(CRM) Asphalt Concrete

Kim, Nak-Seok

Journal of the Korean Society of Hazard Mitigation 2003;3(2):89-98.
Published online June 30, 2003.

폐타이어활용 아스팔트 콘크리트의 실험적 공용특성

김낙석

Experimental Performance Characteristics of Crumb Rubber-Modified(CRM) Asphalt Concrete

Nak-Seok Kim

Abstract

Indirect tensile strength(IDT) test and resilient modulus(Mr) test were performed to evaluate experimental performance characteristics for the conventional and crumb rubber-modified(CRM) asphalt concrete using dry and wet processes asphalt. The IDT test was conducted under three temperatures(5, 10, 20$^{circ}C$). According to the test results, it was shown that indirect tensile strength of CRM asphalt concrete was lower than that of the conventional one. However, toughness and maximum vortical strain of the CRM asphalt concrete were higher than those of the conventional one. The results of Mr test were presented that Mr of CRM asphalt concrete was higher than that of the conventional one. In addition, it was revealed that the overall laboratory performance characteristics of the wet-processed CRM asphalt concrete was better than those of the dry-processed one.

Key Words: CRM; asphalt concrete; dry and wet processes; toughness; indirect tensile strength; resilient modulus; performance characteristic

요지

폐타이어 재활용 아스팔트 콘크리트의 기술개발과 기초 자료의 확립을 위해서 건식공법 및 습식공법으로 생산되어진 폐타이어 재활용 아스팔트 콘크리트와 재래식 밀입도 아스팔트 콘크리트 공시체를 제작하여 아스팔트 혼합물의 내구성을 평가할 수 있는 간접인장강도시험과 회복 탄성계수시험을 수행하였다. 간접인장강도시험 결과 골재 입도의 영향으로 간접인장강도는 재래식 아스팔트 콘크리트가 폐타이어 재활용 아스팔트 콘크리트보다 우수하게 나타났지만, 인성과 최대수직변형률의 경우 골재 입도의 영향에도 불구하고 폐타이어 재활용 아스팔트 콘크리트가 우수하게 나타났다. 또한, 회복 탄성계수시험 결과에서도 폐타이어 재활용 아스팔트 콘크리트가 재래식 아스팔트 콘크리트보다 우수한 성능을 보여줌으로써 폐타이어 재활용 아스팔트 콘크리트의 공학적 특성이 우수하게 나타났다. 특히, 습식공법 활용 폐타이어 재활용 아스팔트 콘크리트의 모든 공용특성은 건식공법활용 혼합물보다 우수한 것으로 평가되었다.

핵심용어: 폐타이어; 아스팔트 혼합물; 건식 및 습식공법; 인성; 간접인장강도; 회복탄성계수; 공용특성