Flexural Experiment of Over Reinforced Prestressed High Performance Fiber Reinforced Concrete Girder

Han, Sang-Mook; Guo, Qing Yong

Journal of the Korean Society of Hazard Mitigation 2011;11(5):91-98.
Published online October 31, 2011.

과보강 프리스트레스트 고강도 섬유보강 콘크리트보 휨실험

한상묵, 궈칭용

Flexural Experiment of Over Reinforced Prestressed High Performance Fiber Reinforced Concrete Girder

Sang-Mook Han, Qing Yong Guo

Abstract

A flexural test of 20 m over reinforced prestressed concrete girder made by high performance fiber reinforced concrete which has 93 MPa compression strength was carried out. To reduce the production cost, domestic fine aggregate, steel fiber which has 0.5 mm diameter and 30 mm long are substituted and silica flour is removed from typical ultra -high peformance concrete mixing portion. Due to the relatively big ultimate compressive strain 0.004 of powder concrete and confinement of volume ratio 2% steel fiber, over reinforced prestressed girder showed 275 mm displacement at 600 kN failure load. Cracking Moment considering the linear relationship of compressive and tensile stress block before crack displayed very close results compared with the test.

Key Words: high performance fiber reinforced concrete; powder concrete; over reinforced prestressed girder; cracking moment; flexural test

요지

압축강도 93 MPa의 고강도 섬유보강 콘크리트를 사용한 길이 20 m의 과보강 프리스트레스트 거더의 휨실험을 수행하였다. 경제적인 제작단가를 위해 전형적인 초고강도 섬유보강 콘크리트 배합성분에서 국내산 규사, 직경 0.5 mm 길이 30 mm 강섬유가 대체 사용되었고, 실리카플로우는 사용되지 않았다. 고강도 분체콘크리트의 상대적으로 큰 0.004의 최대압축변형률과 체적대비 2%대의 강섬유 구속효과으로 인해, 최대 파괴하중 600 kN에서 과보강 프리스트레스트 거더가 중앙단면 처짐 275 mm를 나타내었다. 균열발생 전 인장 및 압축응력 블록의 선형관계를 가정한 균열모멘트는 실험결과와 근접한 결과를 보여주었다.

핵심용어: 고강도 섬유보강 콘크리트; 분체콘크리트; 과보강 프리스트레스트 거더; 균열모멘트; 휨실험