| 하이브리드 섬유보강 초고강도 콘크리트 기둥의 비재하 및 재하 내화시험 |
|
이주하 |
|
|
| Fire Tests of Hybrid Fiber Reinforced Ultra-High-Strength Concrete Columns without and with Loading |
|
Joo Ha Lee |
|
|
|
|
|
|
| Abstract |
|
In this study, fire tests of ultra-high-strength concrete columns without and with column loading were performed to find out the fire resistance method and to evaluate the behavior under high temperature. Full scale column specimens were constructed with hybrid fiber reinforcement of polypropylene, nylon and steel fibers, and then fire tested with a standard heating curve of ISO 834 for 3 hours. From the fire tests, the residual compressive strength, temperature of steel rebar and concrete, spalling and crack patterns were observed and analysed. In addition, the axial deformation of columns subjected to column load was observed during the fire test. The fire test results without and with column load showed that 3 hours fire resistance of 200 MPa ultra-high-strength concrete columns could be obtained by hybrid fiber reinforcement of 0.2, 0.2 and 0.5 vol.% of polypropylene, nylon and steel fibers, respectively. |
| Key Words:
Ultra-high-strength concrete; Hybrid fiber reinforcement; Fire resistance; Column load; Explosive spalling |
| 요지 |
|
본 연구에서는 초고강도 콘크리트의 내화성능 확보 방안을 모색하고 기둥 부재의 화재시 거동을 평가하고자 기둥하중의 비재하 및 재하 조건에서 각각 내화시험을 수행하였다. 폴리프로필렌 섬유, 나일론 섬유, 강섬유를 동시에 혼입하는 하이브리드 섬유보강 방법으로 실물 크기의 기둥 부재를 제작하여 ISO 834 표준가열곡선에 따라서 3시간 내화성능을 평가하였다. 내화시험을 통해 잔존압축강도, 주철근 및 콘크리트 온도, 폭렬 및 균열 양상을 관찰, 분석하였으며, 기둥하중 재하에 따른 축방향 변위도 함께 분석하였다. 비재하 및 재하 내화시험 결과, 폴리프로필렌 섬유 0.2 Vol.%, 나일론 섬유 0.2 Vol.%, 강섬유 0.5 Vol.%의 하이브리드 섬유보강을 통해 200 MPa급 초고강도 콘크리트 기둥의 3시간 내화성능 확보가 가능한 것으로 확인되었다. |
| 핵심용어:
초고강도 콘크리트; 하이브리드 섬유보강; 내화; 기둥하중; 폭렬 |
|